S71020.0

End Mill
Material ID: 6706995

Short series end mill with 2 flutes, diameter 20mm with 38mm length of cut and 100mm overall length, according to DORMER standard with a 20mm plain shank, solid carbide with AlCrN coating, 40° helix and 10° rake angle for slot milling in steel and cast steel, ferritic, martensitic and austenitic stainless steel, cast-iron and high-temperature alloys

info

If you want to see the prices or stock information, please sign in or request access.

Product Feature

Aluminium Chromium Nitride Coating

Hard Material (Solid Carbide)

General Purpose Cutter Type for Low to High Resistance Materials

Cut Length, Short

40° Helix Angle (Flute)

DIN 6535 HA Cylindrical Shank

h9 – Industry Standard Tool Tolerance Zone (based on diameter range)

Radial, Diagonal, Axial

Dormer Standards

Number of Flutes = 2 (teeth)

Product Operation

Shallow Shoulder Milling - Possible use

Plunge Milling - Possible use

Shallow Slot Milling - Primary use

Deep Slot Milling - Primary use

Ramping - Possible use

Drilling - Possible use

Product Detail

Description	Value
EAN number	7320760685440
Product number (SAP)	86022130
Ordering code ANSI	S71020.0
Gross weight - grams	365
Cutting diameter - millimeter (DC)	20 mm
Connection diameter - millimeter (DCON MS)	20 mm
Depth of cut maximum - millimeter (APMX)	38 mm
Overall length - millimeter (OAL)	100 mm
Flute count (NOF)	2
Radial rake angle (GAMF)	10
ISO	S71020.0

Cutting Conditions

P - Steel and cast steel (steels with alloy content ≤ 10% and a hardness of < 45HRC)

P1

P1 - Free machining steel (carbon steels with increased machinability)

navigate_next

	Suitability	v_c	f
P1.1 - Free machining sulfurized carbon steel with a hardness of < 240HB	help_outline Primary use	199 m/min	0.12 mm/rev
P1.2 - Free machining sulfurized and phosphorized carbon steel with a hardness of < 180HB	help_outline Primary use	223 m/min	0.12 mm/rev
P1.3 - Free machining sulfurized/phosphorized and leaded carbon steel with a hardness of < 180HB	help_outline Primary use	230 m/min	0.12 mm/rev

P2

P2 - Plain carbon steel (steels comprised of mainly iron and carbon)

navigate_next

	Suitability	v_c	f
P2.1 - Plain low carbon steel containing < 0.25%C with a hardness of < 180HB	help_outline Primary use	170 m/min	0.12 mm/rev
P2.2 - Plain medium carbon steel containing < 0.55%C with a hardness of < 240HB	help_outline Primary use	150 m/min	0.12 mm/rev
P2.3 - Plain high carbon steel containing > 0.55%C, with a hardness of < 300HB	help_outline Primary use	133 m/min	0.099 mm/rev

P3

P3 - Alloy steel (carbon steels with an alloying content ≤ 10%)

navigate_next

	Suitability	v_c	f
P3.1 - Alloy steel with a hardness of < 180HB	help_outline Primary use	138 m/min	0.12 mm/rev
P3.2 - Alloy steel with a hardness of 180 - 260HB	help_outline Primary use	111 m/min	0.099 mm/rev
P3.3 - Alloy steel with a hardness of 260 - 360HB	help_outline Primary use	94 m/min	0.099 mm/rev

P4

P4 - Tool steel (special alloy steel for tools, dies and molds)

navigate_next

	Suitability	v_c	f
P4.1 - Tool steel with a hardness of < 26HRC	help_outline Primary use	82 m/min	0.099 mm/rev
P4.2 - Tool steel with a hardness of 26 - 39RC	help_outline Primary use	70 m/min	0.099 mm/rev

M - Stainless steel (corrosion resistant steels with ≥ 11% chromium content)

M1

M1 - Ferritic stainless steel (straight chromium non-hardenable alloys)

navigate_next

	Suitability	v_c	f
M1.1 - Stainless steel, ferritic with a hardness of < 160HB	help_outline Primary use	115 m/min	0.12 mm/rev
M1.2 - Stainless steel, ferritic with a hardness of 160 - 220HB	help_outline Primary use	97 m/min	0.12 mm/rev

M2

M2 - Martensitic stainless steel (straight chromium hardenable alloys)

navigate_next

	Suitability	v_c	f
M2.1 - Stainless steel, martensitic with a hardness of < 200HB	help_outline Primary use	102 m/min	0.12 mm/rev
M2.2 - Stainless steel, martensitic with a hardness of 200 - 280HB	help_outline Primary use	84 m/min	0.099 mm/rev

M3

M3 - Austenitic stainless steel (chromium-nickel and chromium-nickel-manganese alloys)

navigate_next

	Suitability	v_c	f
M3.1 - Stainless steel, austenitic with a hardness of < 200HB	help_outline Primary use	94 m/min	0.099 mm/rev
M3.2 - Stainless steel, austenitic with a hardness of 200 - 260HB	help_outline Primary use	81 m/min	0.099 mm/rev

K - Cast Iron (castings of iron and carbon alloys with > 2% carbon content)

K1

K1 - Gray iron (GG) (iron-carbon castings with a lamellar graphite microstructure)

navigate_next

	Suitability	v_c	f
K1.1 - Gray iron, ferritic or ferritic-pearlitic with a hardness of < 180HB	help_outline Primary use	196 m/min	0.12 mm/rev
K1.2 - Gray iron, ferritic-pearlitic or pearlitic with a hardness of 180 - 240HB	help_outline Primary use	145 m/min	0.12 mm/rev
K1.3 - Gray iron, pearlitic with a hardness of 240 - 280HB	help_outline Primary use	109 m/min	0.12 mm/rev

K2

K2 - Malleable iron (GTS/GTW) (heat-treated iron-carbon castings with a graphite-free microstructure)

navigate_next

	Suitability	v_c	f
K2.1 - Malleable iron, ferritic with a hardness of < 160HB	help_outline Primary use	202 m/min	0.12 mm/rev
K2.2 - Malleable iron, ferritic or pearlitic with a hardness of 160 - 200HB	help_outline Primary use	164 m/min	0.12 mm/rev
K2.3 - Malleable iron, pearlitic with a hardness of 200 - 240HB	help_outline Primary use	131 m/min	0.099 mm/rev

K3

K3 - Ductile iron (GGG) (iron-carbon castings with a nodular graphite microsturcture)

navigate_next

	Suitability	v_c	f
K3.1 - Ductile (nodular/spheriodal) iron, ferritic with a hardness of < 180HB	help_outline Primary use	178 m/min	0.12 mm/rev
K3.2 - Ductile (nodular/spheriodal) iron, ferritic or pearlitic with a hardness of 180 - 220HB	help_outline Primary use	136 m/min	0.12 mm/rev
K3.3 - Ductile (nodular/spheriodal) iron, pearlitic with a hardness of 220 - 260HB	help_outline Primary use	110 m/min	0.099 mm/rev

K4

K4 - Austenitic or austempered ductile iron (Ni-Resist/ADI) (iron-carbon alloy castings with an austenitic or ausferrite microstructure)

navigate_next

	Suitability	v_c	f
K4.1 - Austenitic cast iron with a hardness of < 180HB	help_outline Primary use	165 m/min	0.099 mm/rev
K4.2 - Austenitic cast iron with a hardness of 180 - 240HB	help_outline Primary use	125 m/min	0.099 mm/rev
K4.3 - Austempered ductile iron with a hardness of 240 - 280HB	help_outline Primary use	91 m/min	0.099 mm/rev
K4.4 - Austempered ductile iron with a hardness of 280 - 320HB	help_outline Primary use	78 m/min	0.09 mm/rev
K4.5 - Austempered ductile iron with a hardness of 320 - 360HB	help_outline Primary use	65 m/min	0.09 mm/rev

K5

K5 - Compacted graphite iron (CGI) (iron-carbon castings with a vermicular graphite structure)

navigate_next

	Suitability	v_c	f
K5.1 - Vermicular, compacted graphite iron with a hardness of < 180HB	help_outline Primary use	187 m/min	0.099 mm/rev
K5.2 - Vermicular, compacted graphite iron with a hardness of 180 - 220HB	help_outline Primary use	141 m/min	0.099 mm/rev
K5.3 - Vermicular, compacted graphite iron with a hardness of 220 - 260HB	help_outline Primary use	109 m/min	0.099 mm/rev

S - High-temperature alloys (superalloys with high temperature stength and corrosion resistant surpassing that of stainless steel)

S1

S1 - Titanium or titanium alloys

navigate_next

	Suitability	v_c	f
S1.2 - Titanium alloys, with a hardness of 200 - 280HB	help_outline Primary use	69 m/min	0.099 mm/rev

S2

S2 - Fe-based high-temperature alloys

navigate_next

	Suitability	v_c	f
S2.1 - High-temperature Fe-based alloys with a hardness of <200HB	help_outline Primary use	53 m/min	0.09 mm/rev

S3

S3 - Ni-based high-temperature alloys

navigate_next

	Suitability	v_c	f
S3.1 - High-temperature Ni-based alloys with a hardness of <280HB	help_outline Primary use	40 m/min	0.09 mm/rev

S4

S4 - Co-based high-temperature alloys

navigate_next

	Suitability	v_c	f
S4.1 - High-temperature Co-based alloys with a hardness of <240HB	help_outline Primary use	31 m/min	0.09 mm/rev