A1175.2 | A117

A1175.2

Stub Drill
Material ID: 5968044

Stub length drill with straight shank, diameter 5.2mm with an overall length of 62mm and flute length of 26mm according to DIN 1897 standard with 135° split point, cobalt based HSS-E with bronze finish for 2.5xD drilling without pecking in stainless steel and super-alloy

info

If you want to see the prices or stock information, please sign in or request access.

Product Feature

Bronze Tempered (Bronze Oxide) Surface Treatment

High Speed Cobalt Steel Tool Material

DIN 1897 – Stub Drill Standards

2.5×D Usable Tool Depth to Diameter Ratio

Drill Point 135°

Cylindrical Shank / Straight Shank

Standard Spiral Flute Design

Right Hand Rotation / Cutting

h8 – Industry Standard Tool Tolerance Zone (based on diameter range)

Product Detail

Description	Value
EAN number	7320760015544
Product number (SAP)	86009112
Ordering code ANSI	A1175.2
Gross weight - grams	9.42
Cutting diameter - millimeter (DC)	5.2 mm
Cutting diameter - inch (DC)	0.2047 inch
Length chip flute - millimeter (LCF)	26 mm
Overall length - millimeter (OAL)	62 mm
Connection diameter - millimeter (DCON MS)	5.2 mm
Length chip flute - inch (LCF)	1.0236 inch
ISO	A1175.2

Cutting Conditions

P - Steel and cast steel (steels with alloy content ≤ 10% and a hardness of < 45HRC)

navigate_next

P1 - Free machining steel (carbon steels with increased machinability)

navigate_next

	Suitability	v_c	f
P1.1 - Free machining sulfurized carbon steel with a hardness of < 240HB	help_outline Possible use	40 m/min	0.134 mm/rev
P1.2 - Free machining sulfurized and phosphorized carbon steel with a hardness of < 180HB	help_outline Possible use	45 m/min	0.134 mm/rev
P1.3 - Free machining sulfurized/phosphorized and leaded carbon steel with a hardness of < 180HB	help_outline Possible use	46 m/min	0.134 mm/rev

P2 - Plain carbon steel (steels comprised of mainly iron and carbon)

navigate_next

	Suitability	v_c	f
P2.1 - Plain low carbon steel containing < 0.25%C with a hardness of < 180HB	help_outline Possible use	34 m/min	0.134 mm/rev
P2.2 - Plain medium carbon steel containing < 0.55%C with a hardness of < 240HB	help_outline Possible use	30 m/min	0.112 mm/rev
P2.3 - Plain high carbon steel containing > 0.55%C, with a hardness of < 300HB	help_outline Primary use	27 m/min	0.098 mm/rev

P3 - Alloy steel (carbon steels with an alloying content ≤ 10%)

navigate_next

	Suitability	v_c	f
P3.1 - Alloy steel with a hardness of < 180HB	help_outline Possible use	27 m/min	0.112 mm/rev
P3.2 - Alloy steel with a hardness of 180 - 260HB	help_outline Possible use	21 m/min	0.112 mm/rev
P3.3 - Alloy steel with a hardness of 260 - 360HB	help_outline Primary use	18 m/min	0.098 mm/rev

P4 - Tool steel (special alloy steel for tools, dies and molds)

navigate_next

	Suitability	v_c	f
P4.1 - Tool steel with a hardness of < 26HRC	help_outline Possible use	16 m/min	0.112 mm/rev
P4.2 - Tool steel with a hardness of 26 - 39RC	help_outline Primary use	13 m/min	0.098 mm/rev
P4.3 - Tool steel with a hardness of 39 - 45HRC	help_outline Primary use	11 m/min	0.082 mm/rev

M - Stainless steel (corrosion resistant steels with ≥ 11% chromium content)

navigate_next

M1 - Ferritic stainless steel (straight chromium non-hardenable alloys)

navigate_next

	Suitability	v_c	f
M1.1 - Stainless steel, ferritic with a hardness of < 160HB	help_outline Primary use	30 m/min	0.098 mm/rev
M1.2 - Stainless steel, ferritic with a hardness of 160 - 220HB	help_outline Primary use	26 m/min	0.098 mm/rev

M2 - Martensitic stainless steel (straight chromium hardenable alloys)

navigate_next

	Suitability	v_c	f
M2.1 - Stainless steel, martensitic with a hardness of < 200HB	help_outline Primary use	27 m/min	0.098 mm/rev
M2.2 - Stainless steel, martensitic with a hardness of 200 - 280HB	help_outline Primary use	22 m/min	0.098 mm/rev

M3 - Austenitic stainless steel (chromium-nickel and chromium-nickel-manganese alloys)

navigate_next

	Suitability	v_c	f
M3.1 - Stainless steel, austenitic with a hardness of < 200HB	help_outline Primary use	13 m/min	0.134 mm/rev
M3.2 - Stainless steel, austenitic with a hardness of 200 - 260HB	help_outline Primary use	11 m/min	0.134 mm/rev
M3.3 - Stainless steel, austenitic with a hardness of 260 - 300HB	help_outline Primary use	10 m/min	0.134 mm/rev

M4 - Super-austenitic, Duplex or Precipitation Hardening stainless steel (austenitic alloys with > 20% Ni, austenitic-ferritic microstructure or precipitation hardened)

navigate_next

	Suitability	v_c	f
M4.1 - Stainless steel, austenitic-ferritic or super-austenitic with a hardness of < 300HB	help_outline Primary use	15 m/min	0.07 mm/rev

K - Cast Iron (castings of iron and carbon alloys with > 2% carbon content)

navigate_next

K1 - Gray iron (GG) (iron-carbon castings with a lamellar graphite microstructure)

navigate_next

	Suitability	v_c	f
K1.1 - Gray iron, ferritic or ferritic-pearlitic with a hardness of < 180HB	help_outline Possible use	34 m/min	0.196 mm/rev
K1.2 - Gray iron, ferritic-pearlitic or pearlitic with a hardness of 180 - 240HB	help_outline Possible use	25 m/min	0.098 mm/rev
K1.3 - Gray iron, pearlitic with a hardness of 240 - 280HB	help_outline Possible use	19 m/min	0.098 mm/rev

K2 - Malleable iron (GTS/GTW) (heat-treated iron-carbon castings with a graphite-free microstructure)

navigate_next

	Suitability	v_c	f
K2.1 - Malleable iron, ferritic with a hardness of < 160HB	help_outline Possible use	27 m/min	0.098 mm/rev
K2.2 - Malleable iron, ferritic or pearlitic with a hardness of 160 - 200HB	help_outline Possible use	22 m/min	0.098 mm/rev
K2.3 - Malleable iron, pearlitic with a hardness of 200 - 240HB	help_outline Primary use	18 m/min	0.098 mm/rev

K3 - Ductile iron (GGG) (iron-carbon castings with a nodular graphite microsturcture)

navigate_next

	Suitability	v_c	f
K3.1 - Ductile (nodular/spheriodal) iron, ferritic with a hardness of < 180HB	help_outline Possible use	24 m/min	0.098 mm/rev
K3.2 - Ductile (nodular/spheriodal) iron, ferritic or pearlitic with a hardness of 180 - 220HB	help_outline Possible use	18 m/min	0.098 mm/rev
K3.3 - Ductile (nodular/spheriodal) iron, pearlitic with a hardness of 220 - 260HB	help_outline Primary use	15 m/min	0.098 mm/rev

K4 - Austenitic or austempered ductile iron (Ni-Resist/ADI) (iron-carbon alloy castings with an austenitic or ausferrite microstructure)

navigate_next

	Suitability	v_c	f
K4.1 - Austenitic cast iron with a hardness of < 180HB	help_outline Possible use	22 m/min	0.098 mm/rev
K4.2 - Austenitic cast iron with a hardness of 180 - 240HB	help_outline Possible use	17 m/min	0.098 mm/rev
K4.3 - Austempered ductile iron with a hardness of 240 - 280HB	help_outline Primary use	12 m/min	0.098 mm/rev
K4.4 - Austempered ductile iron with a hardness of 280 - 320HB	help_outline Primary use	11 m/min	0.098 mm/rev
K4.5 - Austempered ductile iron with a hardness of 320 - 360HB	help_outline Primary use	9 m/min	0.098 mm/rev

K5 - Compacted graphite iron (CGI) (iron-carbon castings with a vermicular graphite structure)

navigate_next

	Suitability	v_c	f
K5.1 - Vermicular, compacted graphite iron with a hardness of < 180HB	help_outline Possible use	25 m/min	0.098 mm/rev
K5.2 - Vermicular, compacted graphite iron with a hardness of 180 - 220HB	help_outline Possible use	19 m/min	0.098 mm/rev
K5.3 - Vermicular, compacted graphite iron with a hardness of 220 - 260HB	help_outline Primary use	15 m/min	0.098 mm/rev

N - Non-ferrous metals (metals including alloys without an appreciable amount of iron)

navigate_next

N1 - Wrought aluminium

navigate_next

	Suitability	v_c	f
N1.1 - Pure aluminium and wrought aluminium alloys with a hardness of < 60HB	help_outline Possible use	35 m/min	0.196 mm/rev
N1.2 - Wrought aluminium alloys with a hardness of 60 - 100HB	help_outline Possible use	26 m/min	0.196 mm/rev
N1.3 - Wrought aluminium alloys with a hardness of 100 - 150HB	help_outline Possible use	18 m/min	0.175 mm/rev

N2 - Cast aluminium

navigate_next

	Suitability	v_c	f
N2.1 - Cast aluminium alloys with a hardness of < 75HB	help_outline Possible use	48 m/min	0.155 mm/rev
N2.2 - Cast aluminium alloys with a hardness of 75 - 90HB	help_outline Possible use	43 m/min	0.155 mm/rev
N2.3 - Cast aluminium alloys with a hardness of 90 < 140HB	help_outline Possible use	31 m/min	0.155 mm/rev

N3 - Copper or copper alloys

navigate_next

	Suitability	v_c	f
N3.1 - Free-cutting copper-alloys materials with excellent machining properties	help_outline Possible use	68 m/min	0.175 mm/rev
N3.2 - Short-chip copper-alloys with good to moderate machining properties	help_outline Possible use	40 m/min	0.196 mm/rev
N3.3 - Electrolytic copper and long-chip copper-alloys with moderate to poor machining properties	help_outline Possible use	20 m/min	0.155 mm/rev

N4 - Polymers(synthetic or semi-synthetic materials)

navigate_next

	Suitability	v_c	f
N4.1 - Thermoplastic polymers	help_outline Possible use	35 m/min	0.232 mm/rev
N4.2 - Thermosetting polymers	help_outline Possible use	28 m/min	0.196 mm/rev
N4.3 - Reinforced polymers or composites	help_outline Possible use	17 m/min	0.155 mm/rev

S - High-temperature alloys (superalloys with high temperature stength and corrosion resistant surpassing that of stainless steel)

navigate_next

S1 - Titanium or titanium alloys

navigate_next

	Suitability	v_c	f
S1.1 - Titanium or titanium alloys, with a hardness of <200HB	help_outline Primary use	30 m/min	0.112 mm/rev
S1.2 - Titanium alloys, with a hardness of 200 - 280HB	help_outline Primary use	18 m/min	0.098 mm/rev
S1.3 - Titanium alloys, a hardness of 280 - 360HB	help_outline Primary use	10 m/min	0.058 mm/rev

S2 - Fe-based high-temperature alloys

navigate_next

	Suitability	v_c	f
S2.1 - High-temperature Fe-based alloys with a hardness of <200HB	help_outline Primary use	12 m/min	0.098 mm/rev
S2.2 - High-temperature Fe-based alloys with a hardness of 200-280HB	help_outline Primary use	8 m/min	0.058 mm/rev

S3 - Ni-based high-temperature alloys

navigate_next

	Suitability	v_c	f
S3.1 - High-temperature Ni-based alloys with a hardness of <280HB	help_outline Primary use	9 m/min	0.098 mm/rev
S3.2 - High-temperature Ni-based alloys with a hardness of 280 - 360HB	help_outline Primary use	6 m/min	0.058 mm/rev

S4 - Co-based high-temperature alloys

navigate_next

	Suitability	v_c	f
S4.1 - High-temperature Co-based alloys with a hardness of <240HB	help_outline Primary use	7 m/min	0.098 mm/rev
S4.2 - High-temperature Co-based alloys with a hardness of 240 - 320HB	help_outline Primary use	5 m/min	0.058 mm/rev